Product Attributes

Model No.: Wear Plate-HP700T

Brand: HP Plate, HP Welding

Standard: Aisi, Astm, Bs, Din, Gb, Jis

Place Of Origin: China

Species: Steel Plate

Production Process: Cold Rolled

Surface Treatment: Coated

Application: Flange Plate

Special Steel: Wear Resistant Steel, High-Strength Steel Plate

Tolerance: ±1%

Category: Cold Rolled Steel Sheet, Hot-Galvanized Steel Sheet, Low-Alloy Plate, Color Coated Steel Sheet, Hot Rolled Steel Sheet, Steel Plate

Processing Service: Bending, Welding, Decoiling, Cutting, Punching

Standard Size 1: 4.92' X 9.84' Or 1500 X 3000mm

Standard Size 2: 4.59' X 9.84' Or 1400 X 2900mm

Standard Size 3: 3.94' X 9.51' Or 1200 X 2400mm

Standard Size 4: 7.22' X 9.84' Or 2200 X 3000mm

Standard Size 5: 3.28' X 9.84' Or 1000 X 3000mm

Standard Thickness 1: 2on3, 2on4, 3on3, 3on5, 4on6, 6on6

Standard Thickness 2: 7on8, 8on8, 9on10, 10on10, 12on12,10on20

Standard Thickness 3: 9on8, 12on8, 15on10,17on12, 20on12, 25on10

Supply Ability & Additional Information

Packaging: Steel frame & steel belt fastened

Transportation: Ocean,Land,Air

Place of Origin: China

Supply Ability: 50,000㎡ wear plate per year

Certificate: ISO9001: 2015

HS Code: 72109000000

Port: Shanghai,Qingdao,Shenzhen

Payment Type: L/C,T/T,D/P,Paypal,Money Gram,Western Union

Incoterm: FOB,CFR,CIF,EXW,FCA

Packaging & Delivery

Selling Units:

Kilogram

Package Type:

Steel frame & steel belt fastened



Wear Plate Applications~Cement.mp4



HP_ VEDIO 56S



We produce PTAW Tungsten Carbide Overlay Plates as the higher grade of Wear Resistant Steel Plates, see the share from below on product properties

Overlay Details of PTA W Alloy Steel Plate

Item	Casted Angular WC (HV Hardness)	Ni Cr B Si Matrix (HRC Hardness)
Mass Percentage	60%	40%
Elements	W 96%-95.7%, C 3.9-4.2%	Ni, Cr, B, Si, C, Mn, Fe
Hardness	2100-2500 HV	46-50HRC
Mesh	80-270/60-325	80-270/60-325
Thickness	3-25mm depend on overlay dimension and shape
Dimension	According to drawings from customers request
Technology	PTAW with CNC operation program system
Application	Tooth/Adaptor/Shrouds/Liner/Chute (Middle impact force) Iron Mine/Copper Mine/Coal Mine

3.2 Base Steel Q235B: C≤0.20% Mn≤1.4% Si ≤0.35% S ≤0.045 P ≤0.045

3.3 Overly Hardness: 55-60 HRC

4: Overlay Chemistry of Clad Abrasion Steel Plate (40% Ni alloys + 60% WC)

C	Si	Mn	Fe	B		Cr	Ni	W
2.58	1.6	0.04	1.2	1		4.4	33.2	57.6

Quick View On Product

1. Product Name: HP Chromium Carbide Overlay Wear Plate

2. Body Material: A36 Mild Steel + Chromium Carbide Overlay (Hardfacing)

3. Grade: HP700, HP700S, HP750X, HP750P

Wear Resistant Plates

Zigzag Wear Resistant Plates

Smooth Surface Wear Plates

Standard Specifications of HP Wear Plate :

Packing & Delivery of Wear Plate

Packing Way: By Steel Tube, By Steel Belt, By Steel Pallet

Delivery Time: 20 days after order confirmation

Wear Plates Packages On Pallet

Wear Plates Packages

Wear Plates Delivery

Anti-abrasion Comparison_HP Plate vs Other Plate

Company Information

HP Plate (Huifeng Wear Resistant Industry Co., Ltd.) was founded in 1994, as the former Taiwan's Upking-Kurimoto Ltd., led by president Mr. Zhang Kun-Mou, using the world-famous Japanese KURIMOTO hardfacing welding patented technology & welding materials produced by Vautid GmbH. HP Plate has become the most experienced expert specializing in production and sales of wear resistant products.

Wear Plate Production

HP Wear Products Range:

Wear Plate Wear Parts Hardfacing Wire

HP Wear Product Applications

Cement Plant, Mining Site, Steel Mill, Power Generation, Glass Industry,

Dredging, Surgar Industy, Quarry, Construction, etc...where need to be anti-abrasion.

HP Factory Laboratory

Company ISO Certificates:

FAQ On HP Wear Products

Question: Can I cut or drill a hole in an HP overlay plate?

Answer: No. The chromium-carbide layer is not drillable or machineable. When necessary, you may be able to cut it with plasma, waterjet, or arc-gouging.

Question: Is it normal to see cracking in hardfacing plating?

Answer: It depends on the hardfacing alloy. Many chromium carbide alloys check-crack when cooled to moderate temperatures; this is normal. Other alloys, such as the austenitic and martensitic, do not crack when applied properly. Check cracking can be seen as cracking perpendicular to the bead length. This occurs by the high stress that is experienced when the weld metal cools. The cracking stops at the parent metal underneath, as long as the parent metal is not brittle. If the parent metal is hard or brittle, you should choose a buffer layer of a softer, and tougher, weld metal.

Question: What are the most popular applications with hardfacing products?

Answer: The typical applications include Mining Site, Steel Mill, Cement Industry, Power Generation, Glass Industry, Construction, Dredging, Oilsand, etc where need to fight with abrasion and impact.

Question: What metals can be protected with hardfacing?

Answer: Carbon and low-alloy steels with carbon contents of less than 1 percent can be hardfaced. High-carbon alloys may require a special buffer layer. Some of the base metals that can be hardfaced include: stainless steels, manganese steels, cast irons and steels, nickel-base alloys, copper-base alloys.

Question: What is hardfacing?

Answer: Hardfacing is also known as hardsurfacing. It is the process of adding wear-resistant weld metals to the surface of a metal part to protect it from wear and abrasion. Adding the weld metal plates can be achieved through welding or joining.

Tungsten Carbide Wear Abrasion Plate